Analysis of Common Defects of Aluminum Alloy Die Castings

Analysis of Common Defects of Aluminum Alloy Die Castings

2022-07-06 15:01:21

die casting cooling system,die casting surface finish,types of pressure die casting

 

 

Air Oxidation Welds:

 

Air oxidation weld flashes are mostly distributed on the upper surface of the casting, at the corners where the metal mold is not ventilated. The fracture surface is mostly gray-white or light yellow, which can be found by X-ray fluoroscopy or machining, and can also be found in alkali washing, pickling passivation or anodizing treatment.

 

Cause:

 

  • The returning waste is not cleaned up, and the demand for returning waste is too much
  • Poor design of pouring control system
  • The slag in the aluminum alloy liquid is not cleaned up
  • The actual operation of pouring is not good, which leads to the welding bump
  • Insufficient standing time after scouring and metamorphism.

 

Ways to avoid:

 

  • The returned waste should undergo sand blasting, and the demand for returned waste should be moderately reduced
  • Improve the design of the pouring control system and enhance its slag blocking ability
  • Use a moderate solution to remove slag
  • It should be stable when pouring and should pay attention to slag blocking
  • After scouring, the aluminum alloy liquid should be placed for a certain period of time before pouring.

 

Vent bubble

 

The vent holes in the wall of the casting are generally round or oval, with a smooth surface, usually a luminous oxide skin, and sometimes oily yellowish. Surface vent holes and bubbles can be found by sandblasting, and internal vent holes can be found by X-ray fluoroscopy or machining.

 

Air vent bubbles appear grey-black on X-ray film pictures

 

Cause:

 

  • The cast aluminum alloy is unstable and is involved in the vapor
  • Organic chemical residues (such as coal dust, grass-roots entrepreneurial horse manure, etc.) infiltrated into the sand (core)
  • Poor ventilation of metal molds and sand cores
  • There is shrinkage on the surface of cold iron
  • Poor design of pouring control system.

 

Ways to avoid:

 

  • Properly grasp the pouring rate to prevent the vapor from being involved.
  • The organic chemical residues cannot be infiltrated into the molding (core) sand to reduce the air supply of the modeling and design raw materials
  • Improve the working ability of the exhaust pipe of (core) sand
  • Proper adoption and solution of cold iron
  • Improve the design of the pouring control system Three shrinkage porosity Disadvantages: The shrinkage of aluminum alloy die castings generally results in the thick and large position at the root of the fly gate around the inner sprue, the thin-thick wall connection and the thick wall with a large plan.

 

Fracure surface is dark gray

 

In the as-cast state, the fracture surface is dark gray, and the light yellow is grayish white, pale yellow or black gray after tempering treatment. It is cloudy in the X-ray film. The more serious flocculent shrinkage can be obtained according to the high magnification of X-ray and fluorescent light. Inspection methods such as fracture surface

 

Cause:

 

  • Poor gate feeding effect
  • Too much gas supply in the returned waste
  • Over temperature around the inner sprue
  • There is too much water in the sand mold, and the sand core is not air-dried
  • Aluminum alloy crystal is thick
  • The location of the casting in the metal mold is not good
  • The pouring temperature is too high and the pouring rate is too fast

 

Ways to avoid:

 

  • Refill the metal material liquid from the gate to improve the gate design
  • The returned waste should be cleaned for corrosion resistance
  • Set the gate at the shrinkage of the casting, and place the cold iron or the cold iron together with the gate
  • Control sand moisture, and sand core dryness
  • Adopt measures to optimize grain size
  • Improve the position of the casting in the metal mold, reduce the pouring temperature and pouring rate

 

Conclusion

 

For more information about die casting cooling system,die casting surface finish,types of pressure die casting, we are glad to answer for you.

Kontaktujte nás
název

název can't be empty

* E-mailem

E-mailem can't be empty

Telefon

Telefon can't be empty

Společnost

Společnost can't be empty

* Zpráva

Zpráva can't be empty

Předložit